Damage Tolerance Behaviour of Carbon Fibre Multi-axial Warp Knit Fabric Composites
Main Article Content
Abstract
The stitch formation in Multi-axial Warp Knit Fabric (MWKF) is different to that found in traditional overstitching. The effect of such stitching is investigated and reported in this paper. Three different variants of stitch architectures in carbon MWKF, used in an epoxy matrix, were considered to investigate the effect of stitch density. Low energy impact, through penetration impact and compression strength testing were carried out. During low energy impact, a higher stitch density offered more damage resistance, being directly influenced by the through-thickness stitches, which have been shown to stop or deviate crack propagation. Similar results were also found during through penetration impacts. Compression after Impact properties were found to vary directly with the damage area. Whilst a high stitch density resulted in better residual strength properties, the percentage retention of the compression after impact strength was superior for low stitch density MWKF.
Article Details
Issue
Section
Articles
Authors who publish with this journal agree to the following terms: a. Authors retain copyright and grant the journal right of first publication, with the work two years after publication simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal. b. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal. c. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).