Three Dimensional Finite Element Analysis of Rolling Contact between Wheel and Rail
Main Article Content
Abstract
The fatigue performance of the rails is affected by many factors, including service conditions, loading, mechanical properties, environment factors, and manufacturing processes. In this paper, the investigation on wheel-rail to identify the initial damages caused by Rolling Contact Fatigue (RCF) cracks and the location that experienced damages is presented. UIC 54kg rail (grade 900A) was used as the model in three dimensional (3D) finite element contact analysis. The fatigue crack growth on wheel-rail was carried out by considering the Hertz contact pressure. The finite element analysis results show that maximum stress concentration zone was between the wheel-rail surface (rail inside curve gauge corner) and it is above the yield stress limit for wheel-rail steel. Fatigue crack propagation within a depth affected stress concentration region was predicted. The stress intensity factors (SIF) for mode I, mode II and mode III fracture were plotted from ANSYS simulation. Three types of fracture modes were affected the UIC54kg rail Steel to fail or develop initial failure when the crack propagation exceeds 5 mm.
Article Details
Issue
Section
Articles
Authors who publish with this journal agree to the following terms: a. Authors retain copyright and grant the journal right of first publication, with the work two years after publication simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal. b. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal. c. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).