Effect of Heat Treatment and Cryotreatment on the Fatigue Crack Growth in Aluminium 7075 Alloy
Main Article Content
Abstract
Al 7075 is an aluminium alloy with zinc as major element. Al 7075 is commonly used in aircraft components, especially for critical parts like wing and fuselage components. In present investigation Al 7075 has been selected subjected to annealing, cryogenic treatment and the combination of annealing and cryogenic treatment for the study of fatigue crack growth subjected to fatigue load at constant amplitude. Specimens were subjected to fatigue crack growth as per ASTM E-647 standards and the results of fatigue crack growth were compared. NASGRO software was used to predict the fatigue crack growth (FCG) and the results are validated using experimental results. Microstructure analysis of metallic specimens was also carried out to study the micro structural changes in specimens undergoing heat treatment and cryotreatment. From the present investigation it has been observed that cryogenic treatment and heat treatments plays vital role in improving fatigue life of Al 7075 components.
Article Details
Issue
Section
Articles
Authors who publish with this journal agree to the following terms: a. Authors retain copyright and grant the journal right of first publication, with the work two years after publication simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal. b. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal. c. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).